Microstructural evolution in self-catalyzed GaAs nanowires during in-situ TEM study

Abstract

The microstructural evolutions in self-catalyzed GaAs nanowires (NWs) were investigated by using in situ heating transmission electron microscopy (TEM). The morphological changes of the self-catalyst metal gallium (Ga) droplet, the GaAs NWs, and the atomic behavior at the interface between the self-catalyst metal gallium and GaAs NWs were carefully studied by analysis of high-resolution TEM images. The microstructural change of the Ga-droplet/GaAs-NWs started at a low temperature of ~200 °C. Formation and destruction of atomic layers were observed at the Ga/GaAs interface and slow depletion of the Ga droplet was detected in the temperature range investigated. Above 300 °C, the evolution process dramatically changed with time: The Ga droplet depleted rapidly and fast growth of zinc-blende (ZB) GaAs structures were observed in the droplet. The Ga droplet was completely removed with time and temperature. When the temperature reached ~600 °C, the decomposition of GaAs was detected. This process began in the wurtzite (WZ) structure and propagated to the ZB structure. The morphological and atomistic behaviors in self-catalyzed GaAs NWs were demonstrated based on thermodynamic considerations, in addition to the effect of the incident electron beam in TEM. Finally, GaAs decomposition was demonstrated in terms of congruent vaporization.